thickness: 12micron, 15micron, 19micron, 25micron and 30 micron
Beacuse many old packaging machines cannot maintain good perforation quality,which results in seal problems and package quality issues.
provide you with pre-perforated film rolls so there is no need to perforate on your equipment,Our high standard perforation quality
Email : info@prettylift.com Whatsapp Consult(Please click)
| Model | Type | 10um | 12um | 15um | 19um | 25um | 30um |
| 40gauge | 50gauge | 60gauge | 75gauge | 100gauge | 120gauge | ||
| Tensile strength(MD) | N/mm² | 110 | 105 | 100 | 100 | 90 | 80 |
| Tensile strength(TD) | N/mm² | 105 | 100 | 95 | 95/td> | 88 | 75 |
| Elongation(MD) | mm | 115 | 110 | 115 | 115 | 125 | 125 |
| Elongation(TD) | mm | 110 | 105 | 110 | 110 | 120 | 120 |
| Tear MD | g | 7.5 | 7.5 | 11.5 | 14.5 | 20.5 | 22.5 |
| Tear TD | g | 7.0 | 7.0 | 13.5 | 16.0 | 23.0 | 24.0 |
| Seal strength(MD) | N/mm | 0.95 | 0.92 | 1.05 | 1.31 | 1.53 | 1.55 |
| Seal strength(TD) | N/mm | 0.98 | 0.95 | 1.05 | 1.34 | 1.58 | 1.65 |
| Film to Film(Dynamic) | N/mm | 0.25 | 0.25 | 0.24 | 0.24 | 0.27 | 0.27 |
| Film to Film(Static) | N/mm | 0.26 | 0.26 | 0.25 | 0.26 | 0.29 | 0.29 |
| Haze optics | % | 2.2 | 2.2 | 2.6 | 3.2 | 3.9 | 4.5 |
| Clarity | % | 98.5 | 95.5 | 95.5 | 95.5 | 93.5 | 90.0 |
| Gloss @ 45 Deg | % | 85.5 | 83.5 | 85.5 | 82.5 | 80.5 | 79.5 |
| Oxygen Transmission Rate | cc/m²/day | 11300 | 11100 | 10600 | 7000 | 5200 | 4300 |
| Water Vapor Transmission Rate | gm/m²/day | 45.5 | 45.5 | 38.5 | 26.5 | 22.5 | 20.5 |
| Free Shringage(100°C) | % | 21/24 | 20/23 | 29/32 | 18/20 | 26/30 | 30/33 |
| Free Shringage(110°C) | % | 37/40 | 36/49 | 43/46 | 32/34 | 43/46 | 52/55 |
| Free Shringage(120°C) | % | 53/56 | 54/57 | 55/58 | 57/59 | 57/60 | 58/61 |
| Free Shringage(130°C) | % | 64/67 | 63/66 | 64/67 | 62/64 | 63/66 | 64/67 |
| Shrink Tension(100°C) | Mpa | 1.70/2.45 | 1.70/2.45 | 1.70/2.45 | 1.60/2.35 | 1.60/2.35 | 1.60/2.35 |
| Shrink Tension(110°C) | Mpa | 2.60/3.30 | 2.60/3.30 | 2.60/3.30 | 2.50/3.45 | 2.50/3.45 | 2.50/3.45 |
| Shrink Tension(120°C) | Mpa | 2.70/3.50 | 2.70/3.50 | 2.70/3.50 | 2.70/3.40 | 2.70/3.40 | 2.70/3.50 |
| Shrink Tension(130°C) | Mpa | 2.50/3.00 | 2.50/3.00 | 2.50/3.00 | 2.50/2.88 | 2.50/2.88 | 2.50/2.88 |