standard polyolefin shrink film

thickness: 12micron, 15micron, 19micron, 25micron and 30 micron.

Polyolefin film has excellent shrink properties.

Tough centre fold film for use in most shrink machines.

User friendly recyclable product with a very low odour.

Email : info@prettylift.com Skype: prettylift.cn

Overview Specifications

Model Type 10um 12um 15um 19um 25um 30um
40gauge 50gauge 60gauge 75gauge 100gauge 120gauge
Tensile strength(MD) N/mm² 115 110 105 105 93 83
Tensile strength(TD) N/mm² 110 105 100 100/td> 90 78
Elongation(MD) mm 115 110 115 115 125 125
Elongation(TD) mm 110 105 110 110 120 120
Tear MD g 10.5 10.5 14.5 17.5 23.5 25.5
Tear TD g 10.0 10.0 13.5 16.0 23.0 24.0
Seal strength(MD) N/mm 0.65 0.62 0.75 1.01 1.23 1.25
Seal strength(TD) N/mm 0.68 0.65 0.75 1.04 1.28 1.35
Film to Film(Dynamic) N/mm 0.23 0.23 0.22 0.22 0.25 0.25
Film to Film(Static) N/mm 0.24 0.24 0.23 0.24 0.26 0.26
Haze optics % 2.2 2.2 2.6 3.2 3.9 4.5
Clarity % 98.5 95.5 95.5 95.5 93.5 90.0
Gloss @ 45 Deg % 85.5 83.5 85.5 82.5 80.5 79.5
Oxygen Transmission Rate cc/m²/day 11300 11100 10600 7000 5200 4300
Water Vapor Transmission Rate gm/m²/day 45.5 45.5 38.5 26.5 22.5 20.5
Free Shringage(100°C) % 22/25 21/24 30/33 19/21 27/31 31/34
Free Shringage(110°C) % 38/41 37/50 44/47 33/35 44/47 53/56
Free Shringage(120°C) % 54/57 55/58 56/59 58/60 58/61 59/62
Free Shringage(130°C) % 65/68 64/67 65/68 63/65 64/67 65/68
Shrink Tension(100°C) Mpa 1.80/2.55 1.80/2.55 1.80/2.55 1.70/2.45 1.70/2.45 1.70/2.45
Shrink Tension(110°C) Mpa 2.70/3.40 2.70/3.40 2.70/3.40 2.60/3.55 2.60/3.55 2.60/3.55
Shrink Tension(120°C) Mpa 2.80/3.60 2.80/3.60 2.80/3.60 2.80/3.50 2.80/3.50 2.80/3.50
Shrink Tension(130°C) Mpa 2.60/3.10 2.60/3.10 2.60/3.01 2.60/2.98 2.60/2.98 2.60/2.98